What is 16Mo3 material?

Introduction to 16Mo3 material:

16Mo3 steel plate is a pressure vessel EN10028-2 designated grade chromium molybdenum steel alloy used for materials at elevated working temperature, used for manufacturing industrial boilers and weldable steel in stainless steel pressure vessels of petroleum, natural gas and chemical industries.

16Mo3 steel plate is a kind of foreign trademark steel plate, which is different from other raw materials in welding. It needs to be preheated first, and the weld seam should be kept for about 30 minutes after the completion of welding. 16Mo3 manganese steel plate is also an important alloy element of steel, it is an important hardenability element, it has a great influence on the patience of weld metal.

16Mo3 executive standard: European standard EN10028-2

16Mo3 material

16Mo3 material

Chemical composition % of 16Mo3:

C Si Mn Ni P S Cr Mo N Cu
0.12-0.2 max 0.35 0.4-0.9 max 0.3 max 0.025 max 0.01 max 0.3 0.25-0.35 max 0.012 max 0.3

Mechanical properties of 16mo3:

The mechanical properties of 16Mo3 are outlined in the table below.

Grade

Thickness

Temperature (°C)

50

100

150

200

250

300

350

400

450

500

(mm)

MPa

MPa

MPa

MPa

MPa

MPa

MPa

MPa

MPa

MPa

16Mo3

≤16

273

264

250

233

213

194

175

159

147

141

>16 ≤40

268

259

245

228

209

190

172

156

145

139

>40 ≤60

258

250

236

220

202

183

165

150

139

134

>60 ≤100

238

230

218

203

186

169

153

139

129

123

>100 ≤150

218

211

200

186

171

155

140

127

118

113

>150 ≤250

208

202

191

178

163

148

134

121

113

108

Material characteristics of 16mo3:

Heat resistance;

Corrosion resistance;

When the content of Mn is less than 5%, the patience of weld metal is very high;

When the content of Mn is more than 3%, it is brittle again;

When the content of Mn is 60% ~ 180%, the weld metal has higher strength and resistance.